Manufacture of platform chemicals from pine wood polysaccharides in media containing acidic ionic liquids
IDENTIFICADOR UNIVERSAL: http://hdl.handle.net/11093/1878
VERSIÓN EDITADA: https://www.mdpi.com/2073-4360/12/6/1215
TIPO DE DOCUMENTO: article
Pinus pinaster wood samples were subjected to chemical processing for manufacturing furans and organic acids from the polysaccharide fractions (cellulose and hemicellulose). The operation was performed in a single reaction stage at 180 or 190 °C, using a microwave reactor. The reaction media contained wood, water, methyl isobutyl ketone, and an acidic ionic liquid, which acted as a catalyst. In media catalyzed with 1-butyl-3-methylimidazolium hydrogen sulfate, up to 60.5% pentosan conversion into furfural was achieved, but the conversions of cellulose and (galacto) glucomannan in levulinic acid were low. Improved results were achieved when AILs bearing a sulfonated alkyl chain were employed as catalysts. In media containing 1-(3-sulfopropyl)-3-methylimidazolium hydrogen sulfate as a catalyst, near quantitative conversion of pentosans into furfural was achieved at a short reaction time (7.5 min), together with 32.8% conversion of hexosans into levulinic acid. Longer reaction times improved the production of organic acids, but resulted in some furfural consumption. A similar reaction pattern was observed in experiments using 1-(3-sulfobutyl)-3-methylimidazolium hydrogen sulfate as a catalyst.
Ficheros en el ítem