Toxicological evaluation of nanomaterials and their composites with polymers used by the footwear industry.

Abstract

A toxicological evaluation with three different organisms (Daphnia magna, Lemna minor and Raphidocelis subcapitata) and three distinct cell types (Caco-2, Hep-G2 and Raw 246,7) were made for two magnetic nanoparticles (Cobalt ferrite and magnetite) and copper nanowires. These nanomaterials were synthetised by co-precipitation and hydrothermal reaction, respectively, and thought to be used on a blending by extrusion in order to alter the original polymers electrical and thermal conductivity for a future use on the footwear industry.

Se realizó una evaluación toxicológica con tres organismos diferentes (Daphnia magna, Lemna minor y Raphidocelis subcapitata) y tres tipos de células distintos (Caco-2, Hep-G2 y Raw 246,7) para dos nanopartículas magnéticas (ferrita de cobalto y magnetita) y cobre. nanocables. Estos nanomateriales se sintetizaron mediante coprecipitación y reacción hidrotermal, respectivamente, y se pensó que se usarían en una mezcla por extrusión con el fin de alterar la conductividad eléctrica y térmica de los polímeros originales para un uso futuro en la industria del calzado.

Fíxose unha avaliación toxicolóxica con tres organismos diferentes (Daphnia magna, Lemna minor e Raphidocelis subcapitata) e tres tipos de células diferentes (Caco-2, Hep-G2 e Raw 246,7) para dúas nanopartículas magnéticas (ferrita de cobalto e magnetita) e cobre. nanocables. Estes nanomateriais sintetizáronse por co-precipitación e reacción hidrotermal, respectivamente, e créronse que se utilizaban nunha mestura por extrusión para alterar a condutividade eléctrica e térmica dos polímeros orixinais para un futuro uso na industria do calzado.